1. "Melt Extraction" (1) means a process to "solidify rapidly" and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy.
2. "Melt Extraction" (1) means a process to 'solidify rapidly' and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy.
3. "Splat Quenching" (1) means a process to ’solidify rapidly’ a molten metal stream impinging upon a chilled block, forming a flake-like product. N.B.:’Solidify rapidly’ solidification of molten material at cooling rates exceeding 1,000 K/s.
4. "Splat Quenching" (1) means a process to 'solidify rapidly' a molten metal stream impinging upon a chilled block, forming a flake-like product. N.B.:'Solidify rapidly' solidification of molten material at cooling rates exceeding 1000 K/s.
5. "Melt Extraction" (1) means a process to ’solidify rapidly’ and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy. N.B.:’Solidify rapidly’: solidification of molten material at cooling rates exceeding 1,000 K/s. "Melt Spinning" (1) means a process to ’solidify rapidly’ a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:’Solidify rapidly’: solidification of molten material at cooling rates exceeding 1,000 K/s.
6. "Melt Extraction" (1) means a process to 'solidify rapidly' and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s.
7. "Specific tensile strength" (0 1 9) is ultimate tensile strength in pascals, equivalent to N/m2 divided by specific weight in N/m3, measured at a temperature of (296 ± 2) K ((23 ± 2) °C) and a relative humidity of (50 ± 5) %. "Splat Quenching" (1) means a process to ’solidify rapidly’ a molten metal stream impinging upon a chilled block, forming a flake-like product.
8. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s. "Melt Spinning" (1) means a process to 'solidify rapidly' a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s.
9. N.B.:’Solidify rapidly’: solidification of molten material at cooling rates exceeding 1,000 K/s. "Melt Spinning" (1) means a process to ’solidify rapidly’ a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product.
10. Non-metallic particles may be incorporated in the alloy by addition of the appropriate powders. "Melt Extraction" (1) means a process to 'solidify rapidly' and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s. "Melt Spinning" (1) means a process to 'solidify rapidly' a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s. "Microcomputer microcircuit" (3) means a "monolithic integrated circuit" or "multichip integrated circuit" containing an arithmetic logic unit (ALU) capable of executing general purpose instructions from an internal storage, on data contained in the internal storage. N.B.: The internal storage may be augmented by an external storage.
11. It includes the uncorrected systematic deviations, the uncorrected backlash and the random deviations (ref. ISO 10360-2, or VDI/VDE 2617). "Mechanical Alloying" (1) means an alloying process resulting from the bonding, fracturing and rebonding of elemental and master alloy powders by mechanical impact. Non-metallic particles may be incorporated in the alloy by addition of the appropriate powders. "Melt Extraction" (1) means a process to 'solidify rapidly' and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s. "Melt Spinning" (1) means a process to 'solidify rapidly' a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:'Solidify rapidly': solidification of molten material at cooling rates exceeding 1000 K/s.
12. Non-metallic particles may be incorporated in the alloy by addition of the appropriate powders. "Melt Extraction" (1) means a process to "solidify rapidly" and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy. N.B.:"solidify rapidly": solidification of molten material at cooling rates exceeding 1000 K/s. "Melt Spinning" (1) means a process to "solidify rapidly" a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:"solidify rapidly": solidification of molten material at cooling rates exceeding 1000 K/s. "Microcomputer microcircuit" (3) means a "monolithic integrated circuit" or "multichip integrated circuit" containing an arithmetic logic unit (ALU) capable of executing general purpose instructions from an internal storage, on data contained in the internal storage. N.B.:the internal storage may be augmented by an external storage.
13. It includes the uncorrected systematic deviations, the uncorrected backlash and the random deviations (ref. ISO 10360-2, or VDI/VDE 2617). "Mechanical Alloying" (1) means an alloying process resulting from the bonding, fracturing and rebonding of elemental and master alloy powders by mechanical impact. Non-metallic particles may be incorporated in the alloy by addition of the appropriate powders. "Melt Extraction" (1) means a process to ’solidify rapidly’ and extract a ribbon-like alloy product by the insertion of a short segment of a rotating chilled block into a bath of a molten metal alloy. N.B.:’Solidify rapidly’: solidification of molten material at cooling rates exceeding 1,000 K/s. "Melt Spinning" (1) means a process to ’solidify rapidly’ a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:’Solidify rapidly’: solidification of molten material at cooling rates exceeding 1,000 K/s.
14. "Specific tensile strength" (0 1 9) is ultimate tensile strength in pascals, equivalent to N/m2 divided by specific weight in N/m3, measured at a temperature of (296 ± 2) K ((23 ± 2) °C) and a relative humidity of (50 ± 5) %. "Splat Quenching" (1) means a process to "solidify rapidly" a molten metal stream impinging upon a chilled block, forming a flake-like product. N.B.:"solidify rapidly" solidification of molten material at cooling rates exceeding 1000 K/s. "Spread spectrum" (5) means the technique whereby energy in a relatively narrow-band communication channel is spread over a much wider energy spectrum. "Spread spectrum" radar (6) — see "Radar spread spectrum"
15. N.B.:"solidify rapidly": solidification of molten material at cooling rates exceeding 1000 K/s. "Melt Spinning" (1) means a process to "solidify rapidly" a molten metal stream impinging upon a rotating chilled block, forming a flake, ribbon or rod-like product. N.B.:"solidify rapidly": solidification of molten material at cooling rates exceeding 1000 K/s. "Microcomputer microcircuit" (3) means a "monolithic integrated circuit" or "multichip integrated circuit" containing an arithmetic logic unit (ALU) capable of executing general purpose instructions from an internal storage, on data contained in the internal storage. N.B.:the internal storage may be augmented by an external storage.